Polypropylene PP Monofilament Fiber fibers for concrete wall
—Monofilament Form
PP Monofilament fibers PROPERTIES:
Polypropylene fiber for concrete is a polypropylene as the main raw material, adopting unique manufacturing process to make high strength bundle monofilament fiber. Adding into concrete (or mortar) can effectively control concrete (or mortar) micro-cracks which is caused by plastic shrinkage, temperature changes and other factors, to prevent and inhibit the formation and development of cracks, greatly improve crack resistance of concrete, impact resistance and seismic capacity.
PP Monofilament Fiber fibers SPECIFICATIONS:
Raw Material | Polypropylene | Crack Elongation | 20+/-5% |
Fiber Type | monofilament | Fiber Diameter | 20um-30um |
Melting Point(C Deg.) | 160 - 170 | Density(g/cm3) |
0.91+/-0.01
|
Acid &Alkali Resistance | Strong | Tensile Strength(MPa) | 450 min. |
water absorbency |
NO
|
Length: |
Times of 4mm or 6mm |
Normal length |
4mm, 6mm, 8mm, 12mm,18mm, 24mm, 30mm etc... (times of 4mm or 6mm with 1mm more or less ) |
PP Monofilament Fiber fibers APPLICATIONS:
1. Functions:
◆Resist to shrink & crack ◆Increase seepage resistance
◆Increase friction resistance ◆Increase freezing & thawing resistance
◆Improve tendons protection ◆Replace steel net (using in plastering)
◆ Prevent mortar split and crackle expansion
◆Increase impact resistance and peeling resistance
2. Features:
A). No agglomeration and easily spread around in mortar or concrete.
Guarantee the property of crack resistance effectively
B). Apply conveniently. No need to change the proportion of mortar,
and just put the fibers into the mortar mixture and stir for a moment after adding water.
C). Has fine economic property. The equivalent dia. of polypropylene monofilament is only φ
25um, so the ratio of dia. And surface is high and on the basis of crack resistance,
it can reduce the amount (0.6kg/m 3 ) and cut down the cost effectively.
D). Be better to plaster. Because a great number of thin fibers spread into mortar evenly,
so the plastering is much easier and this can improve the binding strength between
surface and base.
E). The fiber has stable chemical property, strong acid &alkali resistance, and can be
used in any engineering projects.
3. Applications:
A). suit for the waterproof layer, floor, inner & outer wall of industrial and civil construction.
B). Increase cracking resistance on the surface of industrial workshop, warehouse and parking lot.
C). Increase cracking & seepage resistance of the ground in natatorium, swimming pool,
pond and ditch.
D). Suit for any mortar projects and common concrete projects.
E). Highway, bridge and other roads.
4. Applying Instruction:
A). Dosage: for resist the common cracks on surfaces, 0.9kg/m3 fibers to cement mortar
Is enough, and for increasing reinforce and seepage resist application
1.8kg/m3 is enough.
B). Stirring requirement: The proportion of cement, sand and aggregate is no
need to be changed. Put cement, aggregate, additive and fiber together,
then stir after adding enough water and time for stirring can be prolonged
for 2~3 minutes in order to make the compound mix completely.
Also it can be mixed with cement and other aggregates in advance,
stirring by adding water at worksite before construction.
PACKING: normal packing is 0.6kg, 0.9kg or 1.0kg a pe film bag,
18kgs/carton or 20kgs/plastic woven bag.
Water soluble paper bag is available.